| Round Bars / Rods(Cold Drawn) |
| Application |
: |
Machined Components, Pump Shafts, Valves, Fasteners, Machine Tools, Dairy Equipments, Surgical & Medical Parts, Threaded Bars, Studs, Bolts, Pins, Hinges and Handles. |
| Grade |
: |
201a, 201b, 201c, 202, 204Cu, 303, 303Cu, 303F, 304, 304Cu, 304L, 310, 316, 316L, 32, 410, 420, 416, 430, 431, 430F & others |
| Condition |
: |
Cold Drawn & Polished Cold Drawn, Centreless Ground & Polished |
| Diameter |
: |
(Size) 2 mm to 12mm (1/8" to 1/2") 6mm to 40mm (1/4" to 1 1/2") |
| Diameter Tolerance |
: |
h9 (Din 671),h11
ASTM A 484 H7, h8, h9 (Din 671) |
| Length |
: |
As per requirement Upto 7 mtrs with a min. length tol. of -0+/100mm As per requirement Upto 7 mtrs with a min. length tol. of -0+/100mm |
|
| We can give Chamfering of 30 or 45 degrees on one or both the ends with our dedicated chamfering machine. |
| |
| ASTM A 479 Stainless Steel Round Bar / Rods Chemical Properties |
| ASTM Grade |
C |
Mn |
Si |
S |
P |
Cr |
Ni |
Mo |
Other |
| 304 |
0.08 max |
2.00 max |
0.75 max |
0.030 max |
0.045 max |
18.0-20.0 |
8.0 11.0 |
- |
- |
| 316 |
0.08 max |
2.00 max |
0.75 max |
0.030 max |
0.045 max |
16.0-18.0 |
10.0 14.0 |
2.0 3.0 |
- |
| 317L |
0.035 max |
2.00 max |
0.75 max |
0.030 max |
0.045 max |
18.0-20.0 |
11.0 14.0 |
3.0 4.0 |
- |
| 310 S |
0.08 max |
2.00 max |
1.5 max |
0.030 max |
0.045 max |
24.0-26.0 |
19.0 22.0 |
3.0 4.0 |
- |
| 347 H |
0.04 0.10 |
2.00 max |
0.75 max |
0.030 max |
0.045 max |
17.0- 19.0 |
9.0 13.0 |
- |
10C(Cb+Ta)<1.10% |
| 321 |
0.08 |
2.00 max |
0.75 max |
0.030 max |
0.045 max |
17.0-20.0 |
9.0 12.0 |
- |
5C 0.70% |
|
| |
| ASTM A 479 Stainless Steel Round Bar/ Rods Physical Properties |
| Tensile Psi (Mpa) |
Yield Psi (Mpa) |
Elongation Strip / Round |
Hardn. |
Reduction in Area (%) |
| 75000 (515) |
30000(205) |
30 |
- |
40 |
| 75000 (515) |
30000 (250) |
30 |
- |
40 |
| 75000 (515) |
30000 (250) |
30 |
- |
40 |
| 75000 (515) |
30000 (250) |
30 |
- |
40 |
| 75000 (515) |
30000 (250) |
30 |
- |
40 |
| 75000 (515) |
30000 (250) |
30 |
- |
40 |
|
| |
|